Title: Determination of true stress corrosion cracking susceptibility index of a high strength Al alloy using glycerin as the non-corrosive atmosphere
Keywords: Composition
High Temperature Effects
Strain Rate
Issue Date: 2004
Publisher: Elsevier
Citation: Scripta Materialia 51(11), 1075-1079
Abstract: The purpose of this work is to show that during slow strain rate testing (SSRT), the laboratory air might not be a non-corrosive atmosphere for evaluating the Iscc (stress corrosion cracking susceptibility index) of high strength Al alloys. Instead, it is proposed that glycerin could be effectively used as the non-corrosive atmosphere to find out the correct Iscc. This is demonstrated while examining 7010 Al alloy in the under aged condition.
URI: 10.1016/j.scriptamat.2004.08.002
ISSN: 1359-6462
Appears in Collections:Article

Files in This Item:
File Description SizeFormat 
4Raja444230.pdf249.14 kBAdobe PDFThumbnail

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.