Title: Melting and defect generation in chemical vapor deposited diamond due to irradiation with 100 MeV Au+ and Ag+ ions
Authors: MISRA, DS
PALNITKAR, UMESH
TYAGI, PK
SINGH, MANOJ K
TITUS, E
AVASTHI, DK
VASA, P
AYYUB, PUSHAN
Keywords: chemical vapor deposition
ion bombardment
diamond
Issue Date: 2006
Publisher: Elsevier
Citation: Thin Solid Films 503(1-2), 121-126
Abstract: Diamond windows prepared using hot filament chemical vapor deposition (CVD) were irradiated with Au and Ag ions of energy 100 and 130 MeV, respectively with fluence in the range 1010 to 3 × 1013 ions/cm2. Scanning electron microscopy (SEM) images showed substantial damage at the surface of the windows irradiated with Au+ of energy 100 MeV and fluence of 3 × 1013 ions/cm2. At some locations on the diamond windows deposited at 16 kPa, the surface layer appeared to have melted and flowed like a liquid exposing small crystallites underneath. Raman spectra of windows after irradiation showed i) a decrease in the intensity of the one-phonon line at 1332 cm− 1 along with an increase in its half width; ii) substantial reduction in the intensity of the graphite G band; and, iii) the appearance of a new band at 667 cm− 1. The band at 667 cm− 1 did not have a corresponding Stokes line and was therefore identified as a photoluminescence (PL) band. The ion induced damage and localized melting of CVD diamond windows are discussed in terms of the thermal spike model.
URI: 10.1016/j.tsf.2005.11.029
http://hdl.handle.net/10054/1247
http://dspace.library.iitb.ac.in/xmlui/handle/10054/1247
ISSN: 0040-6090
Appears in Collections:Article

Files in This Item:

File Description SizeFormat
5548.pdf699.01 kBAdobe PDFView/Open
View Statistics

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - Feedback